Author:  Doug S [ Mon Nov 17, 2014 8:58 am ]
Post subject:  Windshield fabricators hints

Time for a new windshield for 99KK. Last one crazed after about 6 years (I am guessing due to off-gassing of the vinyl dash top). This time I am making my own. I made an oversize mold from old w/s
& will make an oven from insulating board. - It doesn't look too difficult as it it is a flat wrap (what this means is I will probably only have to throw away my first attempt & get it on the second). Any tips or hints on the forming process would greatly be appreciated.

Author:  fytrplt [ Mon Nov 17, 2014 11:02 am ]
Post subject:  Re: Windshield fabricators hints

Forming temperature is critical. Too cold and it will craze, too hot and you get mark-off from the mold. Use flannel to cover the mold. Some people grease the flannel. Probably the most important is the type of Plexiglas you use. I don't recommend Lexan; it is gummy and will eventually cloud up. The local plastic shop probably has a wealth of info on optics and forming temps. Let us know how it goes.

Author:  Rich Brazell [ Mon Nov 17, 2014 1:59 pm ]
Post subject:  Re: Windshield fabricators hints

Check the NL's . Pretty sure there were a couple of articles on how to bend the clear stuff . One even mentioned the use of a local pizza oven ? ???

Author:  Doug S [ Tue Nov 18, 2014 9:36 am ]
Post subject:  Re: Windshield fabricators hints

Thanks for the info. I will take some pics & keep everyone posted on the results.

Author:  lance38dt [ Tue Nov 18, 2014 1:24 pm ]
Post subject:  Re: Windshield fabricators hints

Doug I have had a lexan windshield for 15 years, 7 for the present one, no heating just cut it to size and bend it around. Does scratch a little easier then plexi but it works for me an you can get it tinted and there is some available that is scratch resistant . Also better impact resistant.

Lance 38DT

Author:  jrevens [ Wed Nov 19, 2014 12:28 am ]
Post subject:  Re: Windshield fabricators hints

Lance is right - Lexan (polycarbonate) is tougher, more impact resistant & less prone to cracking, and you can cold bend it. You can even bend it with a sheet metal brake if you need a sharp bend. Some of the newer versions do have a much better scratch resistant surface than plain Lexan. I don't think that they are still as good in that regard as Plexiglas (acrylic), but I'm not up on the latest & greatest. One thing you have to be careful of with Lexan is exposing it to fuel or even concentrated fuel vapor, as it attacks it & causes crazing. You'd want to be careful of splattering or dripping when filling a T-18 tank.